5A06 Aluminum alloy sheet round bar tube wire

5A06 Aluminum alloy sheet round bar tube wire

The content of Mg in 5A06 alloy is the highest, 6.3%, and the content of Mn is 0.65%, and the average total content of Mg and Mn is 7%. Because of its high strength, low plasticity, good corrosion resistance and weldability, can be processed into a plate, tube, rod, profiles, wire and forging die forging, etc., 5A06 aluminum alloy sheet round bar tube wire are widely used in aviation, aerospace, ships, automobiles, ships, missiles, tanks and other industries.

5a06 aluminum

5a06 aluminum alloy

5a06 aluminium

5a06 aluminium

5a06 aluminum alloy

5a06 aluminum

5a06 aluminium

Chemical composition of 5A06 alloy
Alloy Si Fe Cu Mn Mg Zn   Ti Others Al
Each Others
5A06 0.4 0.4 0.4 0.50~0.8 5.8~6.8 0.2 0.0001~0.005 0.02~0.10 0.05 0.15 Remainder

Calibration mechanical strength of 5A06 aluminum alloy sheet round bar tube wire
Technical standard Type Temper δ  or d/mm Tension strength Rm/Mpa Rp0.2/Mpa A/%
YS/T 213
YS/T 215
Aluminum sheet O 0.5~4.5 314 157 15
GB/T 3880 Aluminum sheet O 0.5~4.5 315 155 16
H112 5.0~10.0 315 155 16
GB/T 3880 Aluminum sheet H112 >10.0 305 145 12
>12.5 305 145 12
>25.0 295 135 6
GJB 2662     Aluminum plate  
H112
7~10 315 157 15
>10~25 305 147 11
>25~50 295 137 6
GB/T 3191 Extruded aluminum round bar H112, O ≤200 315 157 15
>200 284 118 10
GJB 2504 Extruded aluminum round bar 5~150 315 157 15
>150 280 120 10
HB 5202 Extruded aluminum round bar ≤240 314 157 15
GJB 2507 Extruded aluminum round bar H112, O All 314 157 15
GB/T 4437 Aluminum tube H112 All 314 147 15
GJB 2381 Aluminum tube H112 >25~150 315 147 12
>180 315 147 10
H112 >25~180 315 147 15
>180 315 147 12
GJB 2379 Cold drawn aluminum tube O All ≤215 ≥88 ≥15
GJB 2351
 
Free forgings、Die forgings H112 As agreed ≥196
≥220

≥10
≥12
GJB 2055, GB/T 3196 Aluminum wire H×8 1.6~10.0 167

technical standard state weight/KG L LT ST HB
Rm/Mpa Rp0.2/Mpa A5/% Rm/Mpa Rp0.2/Mpa A5/% Rm/Mpa A5/%
GJB 2351-1995 H112
O
>60 284 118 11.0 284 118 11.0 284 11.0
>30 294 127 14.0 294 127 14.0 294 14.0
≤30 304 127 14.0 304 127 14.0 304 14.0
HB 5204 O ≤60 304 127 14.0 304 127 14.0 304 14.0 70
>60 284 118 11.0 284 118 11.0 284 11.0 70